摩擦-电化学噪声法研究Mo改性钛合金的腐蚀-磨损行为

1.?

太原理工大学 表面工程研究所, 太原 030024

通讯作者: 范爱兰, fanailan@tyut.edu.cn

收稿日期: 2011-11-29

基金项目: The project was supported by the National Natural Science Foundation of China(51171125),the Science and Research Projects of Shanxi Province, China(20110321051) Shanxi Province Scientific Research Project for Returning Students and School Development Technology Fund of Taiyuan University of Technology
国家自然科学基金项目(51171125)、山西省科技攻关项目(20110321051)、山西省回国留学人员科研项目(2011-038)和太原理工大学校发展科技基金(K201015)资助.

Corrosive-Wear Behavior of Mo Modified Ti6Al4V Alloy by Wear-Electrochemical Noise Method

1.?

Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China

Corresponding author: FAN Ai-lan, fanailan@tyut.edu.cn

Received Date: 29 Nov 2011

引用本文: 张敏, 马永, 张翔宇, 范爱兰, 唐宾. 摩擦-电化学噪声法研究Mo改性钛合金的腐蚀-磨损行为[J]. 摩擦学学报, 2012, 32(3): 301-305.

Citation: ZHANG Min, MA Yong, ZHANG Xiang-yu, FAN Ai-lan and TANG Bin. Corrosive-Wear Behavior of Mo Modified Ti6Al4V Alloy by Wear-Electrochemical Noise Method[J]. TRIBOLOGY, 2012, 32(3): 301-305.

利用等离子表面改性技术在Ti6Al4V合金基体上制备Mo渗镀复合改性层,考察改性层组织结构,利用微动摩擦学试验机并结合电化学噪声技术对比研究基材及改性层在0.5 mol/L NaCl溶液中的腐蚀-微动摩擦学行为,对腐蚀-摩擦过程中的噪声参数进行分析.结果表明:纯Mo改性层能够明显改善钛合金的耐磨和减摩特性;同时提高了合金在0.5 mol/L NaCl溶液中的自腐蚀电位及降低了腐蚀电流,改善了合金表面的腐蚀-摩擦学性能.

关键词: 钛合金, Mo改性层, 微动摩擦, 腐蚀-磨损性能, 电化学噪声
[1]

Wang J B, Wu H H, Jin Z S, et al. Microcrystal growing characters of titania film by MAO[J]. Journal Inorganic Materials,2006,21(3): 731-735.

[2]

Budinski K G. Tribological properties of titanium alloys[J]. Wear,1991,151: 203-217.

[3]

Liu F L, Li J G, Feng Z X. Evolution of surface technologies for titanium alloys[J].Corrosion & Protection,2001, 22(2):54-57(in Chinese)[刘凤岭,李金桂,冯自修.钛合金表面技术的进展[J].腐蚀与防护,2001, 22(2):54-57].

[4]

Li X Y, Fan A L, Tang B, et al.Tribological behavior of molybdenum alloying layer on Ti6Al4V by double glow discharge technique[J]. Tribology, 2003, 23(2):108-111(in Chinese)[李秀燕,范爱兰,唐宾,等. Ti6Al4V表面双层辉光离子渗Mo及其摩擦学性能的研究[J].摩擦学学报,2003,23(2):108-111].

[5]

Tang B, Wu P Q, Li X Y, et al. Tribological behavior of plasma Mo-N Surface modified Ti6-Al4-V alloy[J].Surface and Coating Technology, 2004, 179:333-339.

[6]

Liu D X, He J W. Comparative study on the fretting fatigue and fretting wear behaviors of titanium alloy subject to various surface modifications[J]. Tribology, 2005,25(1):13-17(in Chinese)[刘道新,何家文.经不同表面改性处理的钛合金的微动疲劳和微动磨损行为对比研究[J].摩擦学学报,2005, 25(1):13-17].

[7]

Ding H F, Cui F M, Du X D. Effect of composition and microstructure on impact wear behavior and mechanism of liner steels in corrosive slurry[J]. Tribology, 2005,25(3):221-224(in Chinese)[丁厚福,崔方明,杜晓东.成份和组织对衬板钢在腐蚀料浆环境下的冲击磨损性能与机理的影响[J].摩擦学学报,2005,25(3):221-224].

[8]

Chen J, Yan F Y, Wang J Z. Corrosion wear properties of TC4 titanium alloy in artificial seawater[J]. Tribology, 2012,32(1):1-6(in Chinese)[陈君,阎逢元,王建章. 海水环境下 TC4 钛合金腐蚀磨损性能的研究[J].摩擦学学报,2012,32(1):1-6].

[9]

Dong H, Bloyce A, Morton PH, et al. Surface engineering to improve tribological performance of Ti6-Al4-V[J]. Surface Engineering,1997,13(5):402-406.

[10]

Zhang G Y,Yang L N,Zhang H,et al. The study of the influence mechanism of platinum group and transition metals on the passivation of Ti alloys[J]. Acta Physica Sinica, 2010,59(3):2 022-2 026(in Chinese)[张国英,杨丽娜,张辉,等. 铂族及过渡金属对Ti合金钝化影响机理研究[J].物理学报, 2010,59(3):2 022-2 026].

[11]

Tang B,Fan A L,Qin L,et al. Structure and fretting wear behavior of surface alloying of Ti alloy[J].Nuclear Techniques,2007,30(12):979-982(in Chinese)[唐宾,范爱兰,秦林,等.钛合金表面合金化组织及其微动摩擦学性能研究[J].核技术,2007,30(12):979-982].

[12]

Fan Ai-lan,Qin Lin,Tian Lin-hai, et al. Corrosion resistance of molybdenum nitride modified Ti6Al4V alloy in HCl solution[J]. Journal of Wuhan University of Technology(Materials Science Edition), 2006,23(2): 358-361.

[13]

Qin Yan-mei, Sun Bin-yu, Zhang Xiu-zhi, et al. Corrosion behavior of plasma Mo-N modifled coating on titanium in dilute sulphuric acid solution[J]. Corrosion & Protection,2008, 29(9):514-516(in Chinese)[秦妍梅,孙斌煜,张秀芝,等. 纯钛表面Mo-N共渗改性层在稀H2SO4溶液中的腐蚀行为[J].腐蚀与防护,2008,29(9):514-516].

[14]

Lin N M,Fan A L,Qin L,et al. Corrosion resistance of plasma nitriding layer on pure titanium in artificial saliva[J]. Rare Metals Letters,2008,27(5): 22-26(in Chinese)[林乃明,范爱兰,秦林,等.纯钛离子氮化层在人工唾液中的耐蚀性[J].稀有金属快报,2008,27(5):22-26].

[1]

. 钛合金表面Ti-Al合金扩散层的摩擦性能研究[J]. 摩擦学学报, 2007, 27(3):-305.

[2]

. 钛合金表面双层辉光离子无氢渗碳层摩擦磨损性能研究[J]. 摩擦学学报, 2004, 24(2):-305.

[3]

. 经不同表面改性处理的钛合金的微动疲劳和微动磨损行为对比研究[J]. 摩擦学学报, 2005, 25(1):-305.

[4]

张晓化, 刘道新, 王小锋, 唐宾. TIN / Ti 复合膜与多层膜对Ti811 合金高温摩擦性能及微动疲劳抗力的影响[J]. 摩擦学学报, 2009, 29(4):-305.

[5]

. 面扫描激光淬火对钛合金微动磨损性能的影响[J]. 摩擦学学报, 1999, 19(2):-305.

[6]

. 离心铸造二元钛合金的摩擦磨损性能研究[J]. 摩擦学学报, 2007, 27(3):-305.

[7]

耿浩, 张德坤, 武琳, 陈凯. 钛合金与钴铬钼切向微动磨损行为研究[J]. 摩擦学学报, 2013, 33(6):-305.

[8]

. 钛合金表面掺金属类金刚石薄膜的摩擦磨损性能研究[J]. 摩擦学学报, 2007, 27(4):-305.

[9]

孙建芳, 李傲松, 苏峰华, 李助军. 表面织构钛合金的干摩擦和全氟聚醚油润滑下的摩擦学性能研究[J]. 摩擦学学报, 2018, 38(6):-305. doi: 10.16078/j.tribology.2018111

[10]

方刚, 刘秦, 康志新, 王芳. Ti-6Al-4V钛合金表面疏水性复合膜的制备及其微摩擦磨损性能[J]. 摩擦学学报, 2011, 31(6):-305.

[11]

任佳, 刘秀波, 余鹏程, 陆小龙, 陈瑶, 石皋莲, 吴少华, 徐东. 不同载荷下钛合金激光熔覆Ni60/h-BN自润滑耐磨复合涂层的摩擦学性能[J]. 摩擦学学报, 2015, 35(4):-305. doi: 10.16078/j.tribology.2015.04.008

[12]

. 聚乙烯醇水凝胶/钛合金摩擦磨损特性的正交试验研究[J]. 摩擦学学报, 2007, 27(2):-305.

[13]

. 钛合金表面液相电解类金刚石碳膜的摩擦磨损性能[J]. 摩擦学学报, 2005, 25(3):-305.

[14]

. MoS2/Ti复合薄膜对Ti811合金高温摩擦磨损性能及微动疲劳行为的影响[J]. 摩擦学学报, 2008, 28(3):-305.

[15]

. 摩擦热对Ti6Al4V合金摩擦磨损性能的影响[J]. 摩擦学学报, 2006, 26(3):-305.

[16]

孙奇春, 胡天昌, 樊恒中, 徐仰涛, 张永胜, 胡丽天. 热氧化改性TC4合金在液体润滑条件下的摩擦学行为研究[J]. 摩擦学学报, 2017, 37(4):-305. doi: 10.16078/j.tribology.2017.04.010

[17]

余鹏程, 刘秀波, 陆小龙, 王永光, 陈瑶, 石皋莲, 吴少华. Ti6Al4V合金表面激光熔覆复合涂层的高温摩擦学性能研究[J]. 摩擦学学报, 2015, 35(6):-305. doi: 10.16078/j.tribology.2015.06.013

[18]

. 高速车削钛合金的硬质合金刀具磨损机理研究[J]. 摩擦学学报, 2008, 28(5):-305.

[19]

王兰, 王树奇, 陈康敏, 张秋阳. TC4和TC11合金磨损性能的对比研究[J]. 摩擦学学报, 2015, 35(2):-305. doi: 10.16078/j.tribology.2015.02.013

[20]

. 人牙釉质在人工唾液润滑下与不同偶件对摩时的摩擦学性能研究[J]. 摩擦学学报, 2004, 24(2):-305.

  • 计量
    • PDF下载量 (1570)
    • 文章访问量 (13179)
    • 引证文献数? (0)
    目录

    Figures And Tables

    摩擦-电化学噪声法研究Mo改性钛合金的腐蚀-磨损行为

    张敏, 马永, 张翔宇, 范爱兰, 唐宾