2012, 32(3):238-243.

聚双环戊二烯自润滑材料的高速干摩擦行为

1.?

1. 河南科技大学 高分子科学与纳米技术重点实验室,河南 洛阳 471003

2.?


2. 河南省材料摩擦学重点实验室,河南 洛阳 471003

3.?

河南科技大学 高分子科学与纳米技术重点实验室,河南 洛阳 471003

4.?

河南省材料摩擦学重点实验室,河南 洛阳 471003

通讯作者: 潘炳力, pblhaust@126.com

收稿日期: 2012-01-19

基金项目: This project was supported by the Pre-research Project of National Key Basic Research Program of China (2010CB635113), the National Natural Science Foundation of China (51105130), and Science Foundation of Henan University of Science and Technology (2008ZDYY004).
国家973前期预研项目(2010CB635113)、国家自然科学基金(51105130)和河南科技大学校基金(2008ZDYY004)资助.

Dry Tribological Behaviors of PDCPD Self-Lubricating Materials under High Sliding Speed

1.?

1. Key Laboratory of Polymer Science and Nano Technology, Henan University of Science and Technology, Luoyang 471003, China

2.?


2. Key Laboratory of Tribology of Matericol Tribology, Luoyang 471003, China

3.?

Key Laboratory of Polymer Science and Nano Technology, Henan University of Science and Technology, Luoyang 471003, China

4.?

Key Laboratory of Tribology of Matericol Tribology, Luoyang 471003, China

Corresponding author: PAN Bing-li, pblhaust@126.com

Received Date: 19 Jan 2012

引用本文: 潘炳力, 赵菁, 张玉清, 张永振. 聚双环戊二烯自润滑材料的高速干摩擦行为[J]. 摩擦学学报, 2012, 32(3): 238-243.

Citation: PAN Bing-li, ZHAO Jing, ZHANG Yu-qing and ZHANG Yong-zhen. Dry Tribological Behaviors of PDCPD Self-Lubricating Materials under High Sliding Speed[J]. TRIBOLOGY, 2012, 32(3): 238-243.

采用拟反应注射成型法制备了含油聚双环戊二烯(PDCPD)材料. 利用MMS-1G型摩擦磨损试验机考察了PDCPD材料在摩擦速率处于中高速(5~20 m/s)下的摩擦学性能.结果表明:含油PDCPD材料在中高速干摩擦下,表现出比纯PDCPD更优良的减摩耐磨性能. 纯PDCPD材料的耐磨性受摩擦速率的影响相对较小,而PDCPD含油复合材料对摩擦速率更为敏感. 在较低的摩擦速率下,纯PDCPD的磨损模式呈现明显的磨粒磨损; 较高摩擦速率下,纯PDCPD主要为黏着磨损和微坑损伤. 含油PDCPD材料具有完全不同于纯PDCPD的磨损模式,表现为轻微的表面擦伤和疲劳磨损.

关键词: 聚双环戊二烯, 高速摩擦, 摩擦磨损性能
[1]

Ju Y. Friction and wear behavior of carbon/nitrogen co-permeated layer on mild steel in dry sliding against a bearing steel at an extremely high speed[J]. Tribology, 2002, 22(1): 72-73 (in Chinese)[居毅.碳钢表面碳-氮共渗层在高速干摩擦条件下的摩擦学性能研究[J].摩擦学学报, 2002, 22(1): 72-73].

[2]

Zhang Y Z, Qiu M, Shangguan B, et al. Friction and wear behavior of the materials under very high sliding velocity[J]. Tribology, 2005, 25(4): 343-347 (in Chinese)[张永振,邱明,上官宝, 等. 高速干摩擦条件下铝基复合材料的摩擦磨损行为研究[J]摩擦学学报, 2005, 25(4): 343-347].

[3]

Wang H Q, Wu X Y, Zhou G R, et al. Braking performance of hybrid fibers reinforced brake pad with latex particle modified phenolic resin binder [J]. Tribology, 2011, 31(2):161-168 (in Chinese)[王海庆,吴行阳,周广荣, 等.乳胶粒化学改性酚醛树脂合成闸片的制动性能研究[J].摩擦学学报,2011,31(2):161-168].

[4]

Kang S, Chung D. Improvement of frictional properties and abrasive wear resistance of nylon/graphite composite by oil impregnation [J]. Wear, 2003, 254 (1-2):103-110.

[5]

Pan B L, Du S M, Gao X P, et al.Tribological behavior of polydicyclopentadiene: dry Friction and oil lubrication[J]. Tribology, 2009, 29(6):565-571 (in Chinese)[潘炳力,杜三明,高喜平, 等. 聚双环戊二烯在干摩擦和油润滑条件下的摩擦学性能[J]摩擦学学报, 2009, 29(6):565-571].

[6]

Zhang C F, Pan B L, Zhang Y Q, et al. Tribological properties of polydicyclopentadiene filled with chemically treated expanded graphite[J]. Applied Mechanics and Materials, 2010, 34-35: 1 973-1 977.

[7]

Pan B L, Xing Y L, Zhang C F, et al. Study on erosion wear behavior of PDCPD/MMT nanocomposite[J].Advanced Materials Research, 2010,123-125: 231-234.

[8]

Yan P X, Zhu P, Huang L J, et al. Study on tribological properties of porous polyimide containing lubricants[J]. Tribology, 2008, 28(3): 272-276 (in Chinese)[闫普选,朱鹏,黄丽坚, 等.聚酰亚胺多孔含油材料的摩擦磨损性能研究[J].摩擦学学报,2008,28(3):272-276].

[1]

潘炳力, 杜三明, 高喜平, 张春飞, 张玉清, 张永振. 聚双环戊二烯在干摩擦和油润滑条件下的摩擦学性能[J]. 摩擦学学报, 2009, 29(6):-243.

[2]

. 传动装置密封环摩擦磨损性能研究[J]. 摩擦学学报, 2008, 28(6):-243.

[3]

. 可生物降解二聚酸酯类的合成及其摩擦磨损性能研究[J]. 摩擦学学报, 2005, 25(5):-243.

[4]

乔玉林, 赵海朝, 臧艳, 张庆. 多层石墨烯水分散体系的摩擦磨损性能研究[J]. 摩擦学学报, 2014, 34(5):-243.

[5]

. 纳米Al2O3填充端异氰酸酯基聚丁二烯橡胶-环氧树脂复合涂层的干滑动摩擦磨损性能研究[J]. 摩擦学学报, 2006, 26(4):-243.

[6]

. 火焰喷涂聚苯硫醚(PPS)复合涂层在水环境中的摩擦磨损性能研究[J]. 摩擦学学报, 2005, 25(5):-243.

[7]

. 聚酰亚胺/二硫化钼插层复合材料的制备及其摩擦磨损性能研究[J]. 摩擦学学报, 2005, 25(4):-243.

[8]

. 二硫化钼改性热塑性聚酰亚胺复合材料的摩擦磨损性能研究[J]. 摩擦学学报, 2005, 25(5):-243.

[9]

. 化学表面修饰微球形二硫化钼在液体石蜡中的摩擦磨损性能研究[J]. 摩擦学学报, 2007, 27(1):-243.

[10]

高晓成, 岳文, 王成彪, 李星亮, 王松, 刘家浚. 含二烷基二硫代磷酸锌润滑下等离子渗氮钢的摩擦磨损性能研究[J]. 摩擦学学报, 2011, 31(6):-243.

[11]

. 纳米Cu在聚乙二醇溶液中的摩擦磨损性能研究[J]. 摩擦学学报, 2005, 25(5):-243.

[12]

. 聚四氟蜡和二硫化钼填充凯夫拉纤维织物复合材料的摩擦磨损性能研究[J]. 摩擦学学报, 2007, 27(2):-243.

[13]

. 新型S-N型1,3,4-噻二唑-2-硫酮衍生物对菜籽油摩擦磨损性能的影响[J]. 摩擦学学报, 2007, 27(4):-243.

[14]

胡伟炜, 赵文杰, 曹慧军, 曾志翔, 张昕, 乌学东. 多巴胺改性UHMWPE粉末对环氧涂层韧性及摩擦性能的影响[J]. 摩擦学学报, 2012, 32(5):-243.

[15]

郑帅周, 周琦, 杨生荣, 杨志刚, 王金清. 氟化石墨烯的制备及其作为润滑油添加剂的摩擦学性能研究[J]. 摩擦学学报, 2017, 37(3):-243. doi: 10.16078/j.tribology.2017.03.017

[16]

. 氧气气氛中CrNiMo钢的高温高速干滑动摩擦磨损性能[J]. 摩擦学学报, 2008, 28(4):-243.

[17]

张爱军, 韩杰胜, 苏博, 孟军虎. AlCoCrFeNi高熵合金的高温摩擦磨损性能[J]. 摩擦学学报, 2017, 37(6):-243. doi: 10.16078/j.tribology.2017.06.008

[18]

. 纸基摩擦材料绿色制备工艺与摩擦磨损性能研究[J]. 摩擦学学报, 2004, 24(2):-243.

[19]

. 纳米铜添加剂改善钢-铝摩擦副摩擦磨损性能的研究[J]. 摩擦学学报, 2006, 26(5):-243.

[20]

. 摩擦热对Ti6Al4V合金摩擦磨损性能的影响[J]. 摩擦学学报, 2006, 26(3):-243.

  • 计量
    • PDF下载量 (1647)
    • 文章访问量 (15347)
    • 引证文献数? (0)
    目录

    Figures And Tables

    聚双环戊二烯自润滑材料的高速干摩擦行为

    潘炳力, 赵菁, 张玉清, 张永振